- Wetting of Boron Nitride by Molten Al-Si Alloys
- BN ト ヨウユウ Al Si ゴウキン ノ ヌレ
この論文をさがす
説明
An improved sessile drop method which prevents aluminum from oxidizing, was used in order to obtain accurate values for the contact angles between boron nitride and aluminum or alminum-silicon alloys. The experimental temperature and atmosphere were 1373 K and an purified He+3%H2 mixed gas respectively. The contact angle of each system changed with time through the four phases (I, II, III, IV) similar to other typical ceramic/metal systems. As the quantity of Si increases, the original contact angle (Phase II) decreases. When more than about 11 mass%Si is added, the original contact angle is smaller than 90°. The equilibrium contact angle (Phase IV) increases as the quantity of Si increases. However, it has become clear that the increase in the observed equilibrium contact angle was apparently caused by the crystallization of Si at the solid/liquid/vapor interface and that the true equilibrium contact angle is equal to or around 0 degrees. Therefore, it is concluded from the viewpoint of wetting that the BN/Al-Si system is a suitable combination for fabricating a composite material. Furthermore, the results indicate, when a sessile drop method is used to measure contact angles, the evaporation of the liquid and/or the change in the composition of the liquid can apparently change the contact angles under the conditions where the true contact angles are constant.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 58 (2), 208-214, 1994
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206490511488
-
- NII論文ID
- 130007341175
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
-
- NDL書誌ID
- 3867408
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可