- Single-Phase Interdiffusion in Intermetallic Compound NiAl
- NiAl タン アイチュウ ニ オケル ソウゴ カクサン
この論文をさがす
抄録
Interdiffusion in single-phase NiAl was investigated using a vapor-solid diffusion couple in the temperature range between 1072 and 1572 K. Aluminum was diffused by a chemical transportation technique in which aluminum chloride was used as the carrier gas and consequently NiAl of high aluminum composition was formed on the surface of the NiAl substrate of low aluminum composition. The results obtained showed that interdiffusion coefficients at the temperatures above 1367 K are almost the same as already reported. However, it was found that the interdiffusion coefficients in the composition range around the stoichiometric NiAl at the temperatures between 1072 and 1324 K are extraordinarily small. Particularly, below 1123 K at which little is known, the composition dependence of the diffusion coefficients showed a completely different tendency from that at higher temperatures. The composition range became wider as the temperature decreased. Based on these experimental results, the possibility that a miscibility gap exists in a certain composition range of NiAl phase is discussed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 62 (8), 761-765, 1998
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206491170816
-
- NII論文ID
- 10001970588
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4555444
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可