- High Temperature Deformation of Fine Grained High Purity Alumina
- コウ ジュンド ビサイ タケッショウリュウ アルミナ ノ コウオン ヘンケイ
この論文をさがす
抄録
High-temperature deformation behavior of high-purity polycrystalline alumina (the mean grain size is about 6 μm) prepared with no additive was investigated. In the testing temperature range from 1400 to 1600°C, ductile deformation is obtained at a low strain rate. The ultimate compression stress in each test is decreased with the testing temperature and increased with the strain rate. The strain rate sensitivity is about 0.6 and the apparent activation energy is almost consistent with that of grain boundary diffusion of aluminum ion in the ductile deformation. Stress-enhanced grain growth and nucleation of cavities at grain boundary triple points were observed during the ductile deformation. The increase in area fraction of the cavity is proportional to the strain. It can be speculated that the cavities nucleate and growth at the triple point by nonaccommodated grain boundary sliding.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 62 (8), 748-753, 1998
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206491172864
-
- NII論文ID
- 130007341770
- 10001970539
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4555442
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可