TiCの延性・脆性遷移挙動に及ぼすNbおよびMo添加の効果

DOI Web Site Web Site 被引用文献2件 オープンアクセス
  • 連川 貞弘
    九州大学大学院総合理工学研究科材料開発工学専攻
  • 中島 雅文
    九州大学大学院総合理工学研究科材料開発工学専攻
  • 吉永 日出男
    九州大学大学院総合理工学研究科材料開発工学専攻

書誌事項

タイトル別名
  • Effect of Nb or Mo Addition on Ductile-Brittle Transition Behaviour of Polycrystalline TiC
  • TiC ノ エンセイ ゼイセイ センイ キョドウ ニ オヨボス Nb オヨビ

この論文をさがす

説明

In order to clarify the effect of Nb or Mo addition on ductile-brittle transition behaviour of titanium carbide, sintered TiC, TiC-10 mol%Nb and TiC-10 mol%Mo have been studied using a three-point bending test at temperatures from room temperature to 2020 K, and the fracture surface has been observed by scanning electron microscopy (SEM). It is found that the Nb addition decreases the ductile-brittle transition temperature (DBTT) of TiC by 400 K and increases the ductility, whereas little change of the behaviour was observed when Mo was added. The effect of Nb addition is discussed from the viewpoint of ability for plastic deformation.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 58 (9), 994-1000, 1994

    公益社団法人 日本金属学会