- Evaluation of Hot Corrosion Resistance of Ni-Base Alloys Using Immersion Test, Coating Test and Embedding Test
- シンセキ シケン トフ シケン マイボツ シケン ニヨル Niキ ゴウキン ノ
この論文をさがす
抄録
The hot corrosion resistance of twelve Ni-base alloys was evaluated at 873 K by three different laboratory tests; immersion test, salt coating test and embedding test. In these tests, three different corrosion ashes were employed, a sulfate (Na2SO4-K2SO4-ZnSO4), a chloride (NaCl-KCl-LiCl-CaCl2) and a chloride/sulfate mixture (NaCl-KCl-Na2SO4-K2SO4-ZnSO4). The correlations between the ranking of the corrosion resistance of the alloys in the immersion test, coating test and embedding test were investigated using spearman’s correlation coefficient. The results of the three tests were highly correlated in the sulfate and chloride/sulfate environments, whereas they were relatively poorly correlated in the chloride environment. It was found from the anodic polarization measurement and X-ray difraction analysis of the corrosion products that the relatively poor correlation is attributed to the differences in the rate-determining steps of the corrosion. In the sulfate environment, there was small difference of the corrosion mass loss among the three tests, but in both the chloride and chloride/sulfate environments, the mass losses in the coating test and embedding test were much larger than that in the immersion test. The corrosion mechnisms under the respective corrosion test conditions were discussed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 61 (7), 586-594, 1997
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206491795968
-
- NII論文ID
- 10001966826
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 4267888
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可