I MAによるシリコン中のリン,ヒ素の定量分析

DOI Web Site Web Site

書誌事項

タイトル別名
  • Quantitative Analysis of Phosphorus and Arsenic in Silcon by means of Ion Microanalyzer
  • IMA ニヨル シリコンチュウ ノ リン ヒソ ノ テイリョウ ブンセキ

この論文をさがす

抄録

Experimental study on the analysis of phosphorus and arsenic in silicon has beencarried out with Hitachi IMA-2type ion microanalyzer. It was found that the interfere of 30SiH+ and 29Si30SiO+ peaks were important problem for the analysis. The anal ytical conditions which minimize the production of silicon hydride ions have been studied. The intensity ratio31P+/28Si+on Si wafers(1017-1019 P atoms/cm3)was not propo rtional to the phosphorus concentration determined by wet chemical analysis. But in high concentration range, a normal caribration curve was obtained for P in Phospho silicate glasses with 0.5-7P2O5 mol %.<BR> The intensity ratio75As+/28Si on Si wafers(1016-1020As atoms/cm3)was not proportional to the arsenic concentration determined from the electric resistivities. But at higher concentration than 1020 atoms/cm, the intensity ratio for polycrystalline silicon films was proportional to the arsenic concentration determined by activation analysis. The minimum detectable limit of phosphorus and arsenic in silicon have been esti mated to be nearly 1017-1018 atoms/cm3.

収録刊行物

  • 質量分析

    質量分析 25 (4), 351-362, 1977

    一般社団法人 日本質量分析学会

詳細情報 詳細情報について

問題の指摘

ページトップへ