ハステロイＸ　ＴＩＧ周継手円筒のクリープ特性改良

DOI

書誌事項

タイトル別名
  • Improvement of the Creep Property on Hastelloy X Cylinder with TIG-Welded Joint
  • ハステロイX溶接継手円筒の高温内圧クリープ挙動の研究(第2報)

抄録

The creep rupture strength of TIG-welded Hastelloy X cylinders under internal pressure was remarkable lower than that of non-welded cylinders. In order to improve this strength, tests were performed on the cylinders welded by using various filler wires and welding procedures. The creep rupture strength of these cylinders were, to some extent, improved by using filler wires of Incoloy 800 or Hastelloy X with small boron content. Although the life of cylinders were comparable with that of cylinders without weld joint, several fine cracks were observed on the weld mteal and some of them were penetrated into the wall of the cylinders. The high creep rupture ductility of the weld metal was essential to achieve high reliablity in welded components served at elevated temperatures. The final target of the improvement in creep rupture ductility was discussed.

収録刊行物

  • 溶接学会誌

    溶接学会誌 50 (12), 1158-1164, 1981

    一般社団法人 溶接学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390001206498162304
  • NII論文ID
    130003763584
  • DOI
    10.2207/qjjws1943.50.1158
  • ISSN
    18837204
    00214787
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ