Understanding the Charge Storage Mechanism and Electrochemical Performance on the Poly[Ni(salen)]-modified Electrode Electropolymerized with Different Sweep Rate

DOI Web Site Web Site 参考文献25件
  • LI Xinping
    Department of Physical Chemistry, School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
  • XU Guofeng
    Department of Physical Chemistry, School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
  • DENG Fuhai
    Department of Physical Chemistry, School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
  • CHEN Cheng
    Department of Physical Chemistry, School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
  • LI Jianling
    Department of Physical Chemistry, School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing
  • KANG Feiyu
    Lab of Advanced Materials, Department of Materials Science and Engineering, Tsinghua University

この論文をさがす

説明

Poly[Ni(salen)] films were electropolymerized on multiwalled carbon nanotubes (MWCNTs) in tetrabutylammonium perchlorate/acetonitrile by cyclic voltammetry method. And the employed scan rates were 5, 10, 20 and 40 mV s−1. The effect of sweep rate on the growth of poly[Ni(salen)] was investigated by the apparent surface coverage (Γ) analysis, in which Γ increased almost proportionally with the scan number for all applied scan rates. Fourier transform infrared spectroscopy and field-emission scanning electron microscope images verified the successful deposition of poly[Ni(salen)]. It demonstrated that Ni(salen) were oxidized at the interface between the electrolyte and substrate surface and then the oxidized monomers were cross linked on the substrate. The galvanostatic charge/discharge plots displayed the specific capacitance of 62.8, 78.8, 161.4 and 135.1 F g−1 for 5, 10, 20 and 40 mV s−1 (0.05 mA g−1), respectively. Poly[Ni(salen)] grown at 20 mV s−1 possessed the maximum capacity and decreased as the scan rate increased because the monomer diffusion impeded the growth of poly[Ni(salen)]. The charge diffusion coefficient (D) was found highest with the sweep rate of 20 mV s−1. The excellent electrochemical performance of poly[Ni(salen)] electropolymerized at 20 mV s−1 is ascribed to the better conductivity and superior diffusion ability according to the kinetics.

収録刊行物

  • Electrochemistry

    Electrochemistry 85 (8), 461-468, 2017

    公益社団法人　電気化学会