- Strain Rate Dependence on Bauschinger Effect in Dual Phase Steel Sheet
- Dual Phase コウハン ニ オケル Bauschinger コウカ ノ ヒズミ ソクド イソンセイ
この論文をさがす
抄録
A compression method for sheet metal was developed, and a compression-tension test under high-speed deformation was performed on three kinds of dual-phase steel sheet, such as those with tensile strength grades of 590MPa, 780MPa and 980MPa. Strain rate range was changed from 7.0×10-3[1/s] to 100[1/s]. From the results, the following conclusions were drawn. (1) The dual-phase high-strength steel sheet shows a strain rate dependence on the Bauschinger effect. (2) The strain rate dependence on the Bauschinger effect in the dual-phase steel sheet can be formulated. (3) There is no consistency in the strain rate history dependence on the Bauschinger effect for the dual-phase steel sheet.
収録刊行物
-
- 塑性と加工
-
塑性と加工 51 (594), 674-679, 2010
一般社団法人 日本塑性加工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206499235968
-
- NII論文ID
- 130004488235
- 10026553244
-
- NII書誌ID
- AN00135062
-
- COI
- 1:CAS:528:DC%2BC3cXhtVyktbjK
-
- ISSN
- 18820166
- 00381586
-
- NDL書誌ID
- 10784125
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可