かどすみ肉溶接継手の疲労特性

DOI

書誌事項

タイトル別名
  • Fatigue Properties of Corner Welded Joints under Cyclic Bending Stress

抄録

Fatigue tests were performed on corner welded joints to investigate the effective factors such as jointing method and leg length of weld.<BR>The material used was a structural carbon steel (S35C, 32 mm in thickness). Three type of corner welded joints were chosen as follows, fully lap (type B), half lap (type A) and non lap (type C) corner fillet joints with various leg length. Fatigue tests were carried out under completely reversed plane bending stress at frequency of 1650 cpm. The results were confirmed by FEM stress analysis.<BR>The following conclusions are obtained.<BR>(1) The welded joint of type C shows the highest fatigue strength under cyclic bending stress and the next is type A.<BR>(2) The above results are mainly affected by leg length of welds.<BR>(3) It was found from the FEM stress analysis that the optimum leg length of these corner welded joint was about 80 percent of plate thickness.

収録刊行物

  • 溶接学会誌

    溶接学会誌 51 (7), 599-604, 1982

    一般社団法人 溶接学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390001206499282048
  • NII論文ID
    130003933404
  • DOI
    10.2207/qjjws1943.51.599
  • ISSN
    18837204
    00214787
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ