- Forming of A5052 Aluminum Alloy Sheets by Friction Stir Incremental Forming
- マサツ カクハン インクリメンタル フォーミングホウ ニ ヨル A5052バン ノ セイケイ マサツ カクハン インクリメンタル フォーミングホウ ノ カイハツ ダイ3ポウ
- — Development of Friction Stir Incremental Forming 3rd Report —
- — 摩擦撹拌インクリメンタルフォーミング法の開発 第3報 —
この論文をさがす
抄録
5000 series aluminum alloys do not have sufficient ductility and their applications are limited. To enhance the use of these alloys, it is necessary to develop new forming processes with high formability. The authors have developed a friction stir incremental forming method of forming magnesium alloy sheets without heating and reported on the formability of magnesium alloy sheets at room temperature. In this study, friction stir incremental forming was applied to forming A5052 aluminum alloy sheets, and the formability of these sheets was investigated. Tool rotation rate, tool feed rate and the half apex angle of the pyramidal frustum were changed. Hardness test and tension test on the formed parts were also carried out. A5052 sheets with a 0.5 mm thickness were successfully formed into a pyramidal frustum with a minimum half apex angle of 20°. This result coincides with an elongation of 192% although the fracture elongation of those sheets in the tension test at room temperature was only 14%. The Vickers hardness and tensile strength of the A5052 parts formed by the developed method were decreased compared with those of the unformed ones. Even with added strain by forming, however, the elongation of formed parts was greater than that of the unformed ones owing to the occurrence of grain refinement by dynamic recrystallization during forming.
収録刊行物
-
- 塑性と加工
-
塑性と加工 52 (605), 710-714, 2011
一般社団法人 日本塑性加工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206499763712
-
- NII論文ID
- 10028152283
-
- NII書誌ID
- AN00135062
-
- COI
- 1:CAS:528:DC%2BC3MXps1eku7o%3D
-
- ISSN
- 18820166
- 00381586
-
- NDL書誌ID
- 11163639
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可