The coating on iron castings was prepared using mechanically ground (MG) composite powder consisting of Ni powder and low melting point Ni-P powder as the coating powder with no segregation of the compositions on the mold. Several properties of the coated iron castings obtained were tested. The main results are as follows :<br>(1) Only when the MG time exceeds 36ks, the composite powder becomes even, and use of this powder produces a coating with no segregation of Ni and P. <br>(2) Compared with mixed powder, the composite powder dissolves the castings less. This enable the formation of a Ni rich coating layer with smaller amounts of powder in 10 mm thin castings. This coating showed good performance in salt spray corrosion test.
収録刊行物
-
- 鋳造工学
-
鋳造工学 72 (10), 652-656, 2000
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206506289792
-
- NII論文ID
- 130004556340
- 10005743103
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 5518116
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可