- Extrusion of Rheocast 7075 Aluminum Alloys in Semi-Solid State
- レオキャスト 7075 アルミニウム ゴウキン ノ ハンヨウユウ オシダシ ザ
この論文をさがす
説明
Two kinds of rheocast 7075 aluminum alloy small billets with a fine globular structure or a fine dendrite-dispersed one could be obtained by mechanical stirring at the position extremely near or slightly remote from the solid-liquid interface during solidification, respectively. At ram speed of 1 mm/s, both kinds of the rheocast billets could be extruded in semi-solid states to the round bars with smooth surfaces, while numerous surface cracks reaching inside generated at the case of the billets cast into metal mold. In all billets, extrusions were proceeded by some leaks of liquid phase, which resulted in the lowering of strength for the round bars by the significant loss of solute concentrations as zinc and copper in them. Such liquid leak was suppressed by increasing ram speed to 5 mm/s in the rheocast billet and the hardness of the bars after T6 treatment compared with the one for hot extrusion product.
収録刊行物
-
- 鋳造工学
-
鋳造工学 70 (9), 641-647, 1998
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206506312576
-
- NII論文ID
- 10002554172
-
- NII書誌ID
- AN10514770
-
- COI
- 1:CAS:528:DyaK1cXntFaqsb8%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 4564964
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可