- Observation of Color-etched Primary Austenite Microstructure Phase in Spheroidal Graphite Cast Iron
- チャクショク フショクホウ ニ ヨル キュウジョウ コクエン チュウテツ ノ キョウショウ ギョウコ ショキ ノ オーステナイトソウ ノ カンサツ
この論文をさがす
抄録
A color-etching method has been proposed to reveal the austenite microstructure that precipitates during eutectic solidification of spheroidal graphite cast iron. In fact, the color-etched microstructure corresponds to a phase with a dendritic, or a layer, shape encompassing the spheroidal graphite. To clarify the identity of this color-etched microstructure, we compared the microstructure ?which had been interrupted-quenched during eutectic solidification with a normally solidified microstructure obtained at the same cooling rate.<br> The results show that the color-etched microstructure corresponds to the austenite phase at the middle stage of eutectic solidification. The occurrence of color-etched microstructure was also observed in some commercial castings. Austenite dendrites with various morphologies were observed in every spheroidal graphite cast iron sample. With castings of the same shape, the dendrite structure was found to vary ; Some castings had small dispersed austenite dendrite structures, while others are seen to increase to bulky sizes, suggesting that this hidden austenite dendrite structure affects fluidity during the eutectic solidification process and manifests itself in castability as shrinkage behavior.
収録刊行物
-
- 鋳造工学
-
鋳造工学 81 (10), 482-488, 2009
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206506804352
-
- NII論文ID
- 10025595269
-
- NII書誌ID
- AN10514770
-
- COI
- 1:CAS:528:DC%2BD1MXhsVKgtrfF
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 10462691
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可