- Effect of Melting and Casting Condition on Solidification Segregation of Centrifugally Solidified Ni-hard Cast Iron Roll
- エンシン チュウゾウ ニハード チュウテツ ロール ノ ギョウコ ソシキヘンセキ ニ オヨボス ヨウカイ チュウゾウ ジョウケン ノ エイキョウ
この論文をさがす
抄録
Many sleeves of Ni-hard cast iron in practical roll size were made by the centrifugal casting process and the effects of melting and casting conditions on solidification segregation were investigated. Solidification segregation was found to take place due to non-uniform solidification and the degree of segregation was evaluated by the structure parameter (PDII) that represents the non-uniformity of dendrite structures in coarse and fine regions. Solidification segregation did not generate easily when the PDII value was small. The PDII value decreased when the alloys to adjust the chemical composition were added all together before the first melt-down of the charge material, and when the pouring temperature was low. A lower pouring temperature led to the precipitation of fine and uniform dendrite structures near the surface layer. However, the PDII value increased at the boundary region between the fine dendrite layer and the inner regular dendrite structure, and the non-uniform structure appeared there. The vibration of centrifugal casting greatly promoted the non-uniform solidification.
収録刊行物
-
- 鋳造工学
-
鋳造工学 73 (5), 287-292, 2001
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206506878592
-
- NII論文ID
- 130004556384
- 10007483974
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 5762127
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可