- Microstructure and High Temperature Strength of Fe-25Cr-C-B Eutectic Cast Alloys
- Fe 25Cr C Bケイ キョウショウ ゴウキン ノ ソシキ ト コウオン キョウド
この論文をさがす
説明
Compressive tests were conducted on Fe-25Cr-0C-2.2B, Fe-25Cr-2.2C-1.0B and Fe-25Cr-3.5C-0B eutectic alloys at temperatures up to 1073 K. The results show that the compressive strength of all the as-cast alloys was above 2000 MPa at room temperature and above 100 MPa even at 1073 K. The true stress-true strain curves of the Fe-25Cr-0C-2.2B and Fe-25Cr-3.5C-0B alloys show a large amount of plastic deformation, reflecting the iron matrix deformation. On the contrary, the Fe-25Cr-2.2C-1.0B alloy exhibited fracture immediately after the elastic limit. The compressive strength of the Fe-25Cr-0C-2.2B and Fe-25Cr-3.5C-0B alloys changed in destabilization heat treatment, due to the iron matrix transformation, but the strength of the Fe-25Cr-2.2C-1.0B alloy was only affected slightly by destabilization heat treatment. The effect of destabilization heat treatment more or less disappeared at temperatures above 873 K for each alloy specimen.
収録刊行物
-
- 鋳造工学
-
鋳造工学 73 (5), 311-317, 2001
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206506880768
-
- NII論文ID
- 130004556388
- 10007484025
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 5762248
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可