球状黒鉛鋳鉄の凝固時における温度分析について

DOI Web Site

書誌事項

タイトル別名
  • Temperature Distribution on the Solidification of Spheroidal Graphite Cast Iron
  • 球状黒鉛鋳鉄の凝固時における温度分布について
  • キュウジョウ コクエン チュウテツ ノ ギョウコジ ニ オケル オンド ブンプ ニ ツイテ

この論文をさがす

抄録

  The temperature distribution of test piece of spheroidal and flake graphite Cast iron at solidification has been investigated. </br>  The obtained results were as follows. </br>  1) The solidification time of spheroidal graphite cast iron is longer than that of flake graphite cast iron at equal pouring temperature. </br>  2) The solidification shell of hypo-eutectic flake graphite cast iron develops along mold-wall. On the other hand, the inside shape of solidification shell is parabolic. </br>  3) The spheroidal graphite cast iron solidifies by mushy type, however flake graphite cast iron solidifies by mushy type plus skinformation type. Therfore massfeeding in flake graphite cast iron is easier than in spheroidal graphite cast iron.

収録刊行物

  • 鋳物

    鋳物 38 (6), 372-381, 1966

    公益社団法人 日本鋳造工学会

詳細情報 詳細情報について

問題の指摘

ページトップへ