ねずみ鋳鉄の被削性に及ぼす枯らし及び応力除去焼なましの影響

DOI

書誌事項

タイトル別名
  • Effects of Seasoning and Stress Relief Annealing on Machinability of Gray Cast Iron

説明

  The machinability of gray cast iron is well-knwn to depend on its graphite morphology and matrix structure. However, machinablility occasionally changes even if graphite morphology or matrix structure has not varied. We have therefore focused attention on seasoning and stress relief annealing known to improve machinability without changing the graphite morphology or matrix structure, and carried out machining tests and a series of ultrasonic transmission speed measurements, tensile test, hardness test and structure evaluation while varying the conditions for seasoning and stress relief annealing. As a result, it was found that seasoning applied specimens subject to seasoning greatly vary in machinability despite small changes in the ultrasonic transmission speed, tensile strength, and hardness. Furthermore correlation between ultrasonic transmission speed and amount of machining tool wear was seen in some parts of the stress-relief-annealed specimens with little changes in the optical microstructure and mechanical properties.

収録刊行物

  • 鋳造工学

    鋳造工学 78 (7), 345-350, 2006

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390001206507368576
  • NII論文ID
    130004556583
  • DOI
    10.11279/jfes.78.345
  • COI
    1:CAS:528:DC%2BD28XoslOqur0%3D
  • ISSN
    21855374
    13420429
  • 本文言語コード
    en
  • データソース種別
    • JaLC
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ