- Semi-Solid Processing of Hyper-Eutectic Cast Iron
- ハンギョウコ セイケイ プロセス ニ ヨル コウキノウ カキョウショウ チュウテツ ノ ソウセイ
この論文をさがす
抄録
A series of semi-solid processing experiments were carried out under various conditions to clarify the effects of stirring condition and quenching temperature for hyper-eutectic cast iron. A characteristic cast structure was obtained when the slurry was cooled with stirring within the temperature region where the ternary phase coexists. Proper stirring of the semi-solid cast iron yielded microstructure, with uniformly distributed fine graphite and eutectic cell. Semi-solid processed hyper-eutectic cast iron gives reasonable mechanical strength and elongation values with good wear resistance, compared to hyper-eutectic cast iron obtained normally. In addition, functionally gradated cast iron was obtained by carburizing during the stirring of semi-solid hypo-eutictic cast iron. The microstructure, carbon content and mechanical properties are gradated from the inside to the outside of the specimen. Semi-solid processing cast iron has promising prospects for application in many industrial fields because of their attractive properties.
収録刊行物
-
- 鋳造工学
-
鋳造工学 73 (11), 721-726, 2001
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206507891456
-
- NII論文ID
- 10007484590
-
- NII書誌ID
- AN10514770
-
- COI
- 1:CAS:528:DC%2BD38Xps1KitA%3D%3D
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 5972307
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可