多合金系自義鉄の連続冷却変態挙動に及ぼすバナジウム量の影響

DOI Web Site 被引用文献1件 参考文献12件

書誌事項

タイトル別名
  • Influence of Vanadium Content on Continuous Cooling Transformation Behavior of Multi-component White Cast Iron
  • 多合金系白鋳鉄の連続冷却変態挙動に及ぼすバナジウム量の影響
  • タゴウキンケイ ハク チュウテツ ノ レンゾク レイキャク ヘンタイ キョドウ ニ オヨボス バナジウムリョウ ノ エイキョウ

この論文をさがす

抄録

  Influence of V content in multi-component white cast iron, which contains 5 mass% main alloying elements of Cr, Mo, W, each and 2 mass% of C and Co, on continuous cooling transformation behavior was investigated by varying the V content from 3 mass% to 9 mass%. The austenitizing temperatures used in this experiment were 1273 K and 1373 K.<br>  In the irons with up to 7 mass%V, both pearlite and bainite transformations appeared in CCT diagram, but in the iron with 9 mass%V, only transformation of ferrite precipitation was seen.<br>  The critical cooling rate of pearlite transformation (V C-P) decreased from 0.56 K/s to 0.11 K/s at 1273K austenitization and from 0.43 K/s to 0.06 K/s at 1373 K austenitization respectively, as the V content increased up to 7 mass%. The critical cooling rate of bainite transformation (V C-B) decreased with an increase in V content up to 4 mass%, but it increased over 4 mass%V.<br>  Though the Ms temperature did not change much between the irons with 3 mass%V and 4 mass%V, it gradually rose with an increase in the V content over 4 mass%, regardless of the austenitizing temperature. Mf temperature appeared first in the 5 mass%V iron at 1273K austenitization and in the 7 mass%V iron at 1373K austenitization, respectively, and then it rose corresponding to the increase of the V content.<br>  The highest macro-hardness of transformed specimen increased once and then gradually decreased as the V content increased. The V content at the maximum hardness was about 5 mass%.

収録刊行物

  • 鋳造工学

    鋳造工学 77 (5), 301-307, 2005

    公益社団法人 日本鋳造工学会

被引用文献 (1)*注記

もっと見る

参考文献 (12)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ