- Joining of Alumina to Spheroidal Graphite Cast Iron Using Spattered Ag-Cu-Ti Alloy
- スパッタリング シタ Ag Cu Ti ゴウキン ニ ヨル アルミナ ト キュウジョウ コクエン チュウテツ ノ セツゴウ
この論文をさがす
抄録
The effects of spattered film thickness and reaction layer on the shear strength of Al2O3 - spherical graphite cast iron (FCD400) joints were studied using spattered Ag-Cu-Ti alloy. Reaction products formed at the interface between Al2O3 and spattered Ag-Cu-Ti alloy were investigated by scanning electron microscope and Auger electron microscopy. The shear strength of 243-268 MPa was obtained at the Al2O3 - FCD400 joints brazed at 1123 K for 600 s using spattered Ag-Cu-Ti alloy of about 7000 nm in film thickness. Two reaction layers Ti3.9(Cu, Al)2.5O3.4 and Ti2.1(Cu, Al)3.6O2.5 were formed at the interface between the spattered Ag-Cu-Ti alloy and Al2O3, depending on the spattered Ti film thickness.
収録刊行物
-
- 鋳造工学
-
鋳造工学 75 (9), 600-604, 2003
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206507952256
-
- NII論文ID
- 10013907835
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 6702314
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可