カルシアるつぼによるTi-6Al-4V合金の溶解と鋳造欠陥

書誌事項

タイトル別名
  • Melting of Ti-6Al-4V Alloy Using CaO Crucible and Internal Defects of its Castings
  • 技術報告 カルシアるつぼによるTi-6Al-4V合金の溶解と鋳造欠陥
  • ギジュツ ホウコク カルシアルツボ ニ ヨル Ti 6Al 4V ゴウキン ノ ヨウカイ ト チュウゾウ ケッカン

この論文をさがす

抄録

The CaO crucible is expected to serve as a useful tool for melting Ti and its alloys due to its thermodynamic stability. However, there still remain problems that need to be resolved in the melting of Ti and its alloys to enable commercial use. <br>  The causes of the defects of Ti-6Al-4V alloy castings melted in the CaO crucible were examined and compared with induction skull melting. The key factors of the melting technique using the CaO crucible, affecting the quality of Ti-6Al-4V alloy castings, were investigated. <br>  Defects of the Ti-6Al-4V alloy castings are caused by the chemical reduction of CaO by Ti. Pressurizing with argon gas in a vacuum induction chamber is effective for reducing the defects. Preheating of the charged material in the crucible and quick pouring into a mold of lower temperature, just after melting down, are important for producing sound Ti-6Al-4V castings.

収録刊行物

  • 鋳造工学

    鋳造工学 75 (11), 769-776, 2003

    公益社団法人 日本鋳造工学会

参考文献 (17)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ