シルジン青銅鋳物JIS CAC804の鋳造性, 機械的性質, 耐食性へのすず添加の影響

DOI Web Site

書誌事項

タイトル別名
  • Influence of Sn Addition on Castability, Mechanical Properties and Corrosion Resistance of JIS CAC804 Silzin Bronze Castings
  • シルジン セイドウ イモノ JIS CAC804 ノ チュウゾウセイ,キカイテキ セイシツ,タイショクセイ エ ノス ズテンカ ノ エイキョウ

この論文をさがす

説明

<p>  The influence of Sn addition on castability, mechanical properties, and corrosion resistance of silzin bronze castings JIS CAC804 was investigated. The results showed that the solidus point and liquidus point are lowered by Sn addition and the solidification temperature range is wide. Generally, castability is poor when the solidification temperature range is wide, but there were no significant differences between CAC804 and Sn-added CAC804. Moreover, grain refinement during melt-solidification decreases casting defects like shrinkage cavities. </p><p>  The added Sn transforms the solid solution into the γ phase, and decreases ductility. Although the results of erosion corrosion tests differ according to test conditions, it is clear that Sn addition decreases the weight of CAC804 in erosion corrosion tests under the two different conditions.</p>

収録刊行物

  • 鋳造工学

    鋳造工学 87 (12), 844-848, 2015

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ