Suppression of Blooming by Amorphous Resins.

DOI Web Site 13 References

Bibliographic Information

Other Title
  • 難燃剤テトラブロモビスフェノールＡ‐ビス（２，３‐ジブロモプロピル）エーテル添加ポリプロピレン組成物におけるブルーミング現象メカニズムの解明　１　　非晶樹脂添加によるブルーミング抑制
  • ヒショウ ジュシ テンカ ニ ヨル ブルーミング ヨクセイ

Search this article

Description

In the tetrabromobisphenol A-bis (2, 3-dibromopropyl ether) (TBA-DB) and polypropylenes (PP) system, the blooming was suppressed by the addition of ethylene/vinyl acetate copolymer (EVA) to PP, and the relation between the EVA content necessary for the suppression of blooming and the TBA-DB content was determined. The appropriate temperature of blooming acceleration test for injection molding was not generally high but moderate around 50°C. A general acceleration test could be applied to the phenomenon where the reaction rate obeys the Arrhenius equation and was accelerated by elevating temperature. In the case of injection moldings a similar behavior to that of a solution where a solute dissolves in a solvent was observed in their blooming phenomenon. Namely, at high temperatures, the solubility is high and the precipitating (blooming) material is scarce (or absent). On the other hand, at low temperatures, although the precipitating material is abundant, the transportation rate is low and hence the blooming does not occur. The most appropriate temperature was determined to be around 50°C on a balance of the above-mentioned compensating effects.

Journal

  • KOBUNSHI RONBUNSHU

    KOBUNSHI RONBUNSHU 58 (9), 453-461, 2001

    The Society of Polymer Science, Japan

References(13)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top