ビスイソプロピルキサントゲンの存在下におけるスチレンのラジカル重合

DOI Web Site

書誌事項

タイトル別名
  • Radical Polymerization of Styrene in the Presence of Bis (isopropyl xanthogen)
  • ビスイソプロピルキサントゲン ノ ソンザイカ ニ オケル スチレン ノ ラジカ

この論文をさがす

抄録

Radical polymerization of styrene (St) in the presence of bis (isopropyl xanthogen), CH3CH (CH3) -OC (S) -SS-C (S) O-CH (CH3) CH3 (BX), was carried out in benzene at 70°C. The number of the xanthate (X) end groups per polymer molecule (Na/2) decreased with increasing conversion except the case of high feed ratio of [BX] 0/ [St] 0. The chain transfer constant was determined to be 4.43 by measuring both the number-average degree of polymerization and the sulfur content extrapolated to zero conversion. Hydrolyses of the X end groups in polymers with ethanolic potassium hydroxide or morpholine in nitrogen atmosphere proceeded smoothly and completely. However, it was found that the hydrolyzed polymers contained only about 70% of the theoretical amount of mercapto end groups, and they had molecular weights which corresponded to the consumed amount of the mercapto groups. Copolymerizations of St with divinyl benzene in the presence of BX proceeded to a high conversion without gelation under suitable conditions. The (Na/2) values of copolymers were considerably higher than those of the homopolymers and by oxidation the hydrolyzed copolymers were converted to insoluble copolymers.

収録刊行物

  • 高分子論文集

    高分子論文集 34 (2), 97-102, 1977

    公益社団法人 高分子学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ