ポリエチレンの紫外線劣化　Ｉ　　赤外線吸収スペクトルからみたポリエチレンの劣化機構

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • Degradation Mechanism of Polyethylene by Infrared Analysis
  • セキガイセン キュウシュウ スペクトル カラ ミタ ポリエチレン ノ レッカ

この論文をさがす

説明

Photodegradation of high-density polyethylene (HDPE) exposed in a weathermeter has been investigated from the relation between yield strength or elongation and the concentrations of various functional groups. The amount of the functional groups in the degraded polyethylene exposed in a Sunshine carbon ark weathermeter was accurately measured with a Fourier-transformed infrared spectroscopy. The decrease of elongation in HDPE was not proportional to the concentration of carbonyl group. The mechanism was estimated as follows. (1) The decrease in the elongation of polyethylene without UV absorber is caused mainly by the scission of the main chain. (2) The decrease in elongation of the polyethylene stabilized with UV absorber is related mainly to the formation of crosslinking. From these results, molecular weight, molecular weight distribution and / or gel fraction are considered to be proper parameters for the photodegradation of HDPE compared with the concentration of carbonyl groups.

収録刊行物

  • 高分子論文集

    高分子論文集 35 (7), 429-433, 1978

    公益社団法人 高分子学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ