- 山崎 信助
- 工業技術院化学技術研究所
書誌事項
- タイトル別名
-
- Formation of Ultrafine Polymer Latex by Emulsion Polymerysation Process
- ニュウカ ジュウゴウホウ ニヨル チョウ ビリュウシ ポリマー ラテックス ノ
この論文をさがす
抄録
Some problems in the formation of poly (methyl methacrylate) latex with very fine particles have been investigated. Transparent polymer latices having particle sizes of approximately 0.02-0.03μ diameter were produced by use of sodium lauryl sulfate as an emulsifier and by adding a small amount of cupric ion in a K2S2O6-Na2S2O3 redox initiating system. When a very fine polymer latex is produced by emulsion polymerisation nuder conventional conditions, the latex viscosity usually increases up to several hundred thousand centi poise in the gel state. It was found that the addition of an electrolyte of a limited concentration to the ultrafine polymer latex remarkably reduced the apparent viscosity: the viscosity of more than several hundred thousand centi poise was decreased to about several centi poise. Change in the fluidizing character of the latex with very high viscosity by the electrolyte addition can be explained by means of destruction of an ice-like hydration shell with sufficient thickness for the close-packing and of the concept of the effect of particle spacing on the latex viscosity introduced by the Kelsey's calculation method.
収録刊行物
-
- 高分子論文集
-
高分子論文集 36 (11), 729-737, 1979
公益社団法人 高分子学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206523987328
-
- NII論文ID
- 130003836662
-
- NII書誌ID
- AN00085011
-
- ISSN
- 18815685
- 03862186
-
- NDL書誌ID
- 2070149
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可