加硫ゴム表面にブリード・固着化させたワックスのオゾン遮断効果

DOI Web Site Web Site 参考文献8件 オープンアクセス

書誌事項

タイトル別名
  • Ozone Resistance of Wax Adhered after Bled onto Surface of Vulcanized Rubber
  • カリュウゴム ヒョウメン ニ ブリード ・ コチャクカ サセタ ワックス ノ オゾン シャダン コウカ

この論文をさがす

説明

<p>Effect of wax on ozone degradation of vulcanized rubber was investigated at temperatures between -30 °C and 40 °C. The vulcanized rubber was prepared by mixing synthetic isoprene rubber with CB, sulfur, ZnO, stearic acid, accelerator and wax, followed by heating at 160 °C for 8 min. It was further heated at 23 °C, 40 °C and melting temperature of each wax for 72 hours under 20% stretching, in order to segregate the wax onto the surface of the vulcanized rubber as a bleeding. Ozone exposure tests of the vulcanized rubber were carried out at the temperatures between -30 °C and 40 °C in the presence of 50 pphm ozone for 24 and 168 hours, respectively. Crack propagation of the ozone-degraded rubber was observed with a digital microscope. The wax, bleeding onto the surface of the vulcanized rubber, was found to improve the ozone resistance of the rubber as compared with an ordinary bloomed wax.</p>

収録刊行物

  • 日本ゴム協会誌

    日本ゴム協会誌 90 (10), 463-469, 2017

    一般社団法人 日本ゴム協会

参考文献 (8)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ