The New Concept for Electrowinning Process of Liquid Titanium Metal in Molten Salt
-
- TAKENAKA Toshihide
- Faculty of Engineering, Toyohashi University of Technology
-
- SUZUKI Takayuki
- Graduated from Toyohashi University of Technology Present application: Mitsubishi Motors Corporation
-
- ISHIKAWA Masahiro
- Faculty of Engineering, Toyohashi University of Technology
-
- FUKASAWA Eiichi
- Sponge Titanium Division, Toho Titanium Co. Ltd.
-
- KAWAKAMI Masahiro
- Faculty of Engineering, Toyohashi University of Technology
書誌事項
- タイトル別名
-
- New Concept for Electrowinning Process of Liquid Titanium Metal in Molten Salt
この論文をさがす
抄録
<p>Direct electrowinning of liquid titanium metal has been investigated by using a DC-ESR (Direct Current Electro Slag Remelting) apparatus. A small scale DC-ESR unit was operated in a DC reverse polarity mode, where a graphite rod was used as anode and a steel or a copper base-plate was used as cathode. The used salt was CaO-CaF2-TiO2 mixture. The distance between the cathode and the anode was essential to the electrolysis. A metal pool was formed on the base-plate and the current efficiency for the reduction was up to 18% with the proper distance between the electrodes. Some amount of titanium was electrodeposited on the base-plate though its state changed with the electrolytic condition. Pure titanium metal pieces were obtained in the solidified salt after the run with the bigger distance. It is concluded that the electrowinning of liquid titanium metal by the present process is possible if sufficient heat to form a metal pool can be supplied at the bigger distance between the electrodes.</p>
収録刊行物
-
- Electrochemistry
-
Electrochemistry 67 (6), 661-668, 1999-06-05
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001277393473408
-
- NII論文ID
- 10002567675
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
- http://id.crossref.org/issn/13443542
-
- NDL書誌ID
- 4743914
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可