Thermoelectric Properties of p-Type Half-Heusler Compounds FeNb₀.₉M₀.₁Sb (M = Ti, Zr, Hf)
-
- Silpawilawan Wanthana
- Graduate School of Engineering, Osaka University
-
- Ohishi Yuji
- Graduate School of Engineering, Osaka University
-
- Muta Hiroaki
- Graduate School of Engineering, Osaka University
-
- Yamanaka Shinsuke
- Graduate School of Engineering, Osaka University
-
- Kurosaki Ken
- Graduate School of Engineering, Osaka University Research Institute of Nuclear Engineering, University of Fukui JST, PRESTO
書誌事項
- タイトル別名
-
- Thermoelectric Properties of <i>p</i>-Type Half-Heusler Compounds FeNb<sub>0.9</sub><i>M</i><sub>0.1</sub>Sb (<i>M</i> = Ti, Zr, Hf)
この論文をさがす
抄録
<p>Recently, it has been reported that Hf-substituted Fe(Nb1−xHfx)Sb-based p-type half-Heusler compound exhibits exceptionally high thermoelectric (TE) figure of merit zT = 1.5 at 1200 K [C. Fu et al.: Nat. Commun. 6 (2015) 8144.]. However, the effect of substitute elements on the TE properties of FeNbSb is still unclear. Here, we synthesized polycrystalline samples of Fe(Nb0.9M0.1)Sb (M = Ti, Zr, Hf) by arc-melting followed by spark plasma sintering, and examined their high-temperature TE properties. The Ti-substituted sample was nearly single phase while the Zr- and Hf-substituted samples contained small amounts of secondary phase. The Ti-substituted sample exhibited the best TE performance. In the present case, Ti is better substituted element than Zr and Hf for enhancement of TE properties of FeNbSb.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 59 (7), 1030-1034, 2018-07-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001288038284928
-
- NII論文ID
- 130007410483
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 029074179
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可