Cross tension strength of Al alloy/ CFRP dissimilar friction lap spot joint

DOI Web Site
  • KURABE Yohei
    National Institute of Technology, Ishikawa College Dept. of Mechanical Engineering
  • IZUMINO Koji
    National Institute of Technology, Ishikawa College Dept. of Mechanical Engineering
  • MIYASHITA Yukio
    National Institute of Technology, Ishikawa College Dept. of Mechanical Engineering
  • HORI Hisashi
    Nagaoka University of Technology, Dept. of Mechanical Engineering
  • HORI Hisashi
    Nippon Light Metal Company Ltd.

Bibliographic Information

Other Title
  • Al合金/CFRP異材摩擦重ね点接合継手の十字引張強度

Abstract

<p>The aim of this study is to investigate effect of plunging depth of welding tool on cross tension strength of Al alloy/CFRP friction lap spot joint. In this study, thermoplastic sheet was set between Al alloy and CFRP in order to join carbon fiber reinforced thermoset to Al alloy. In welding process, frictional heat is generated by contact between rotating welding tool and Al alloy. Generated heat is transferred from Al alloy to thermoplastic sheet. The thermoplastic sheet is melted and bonded to both Al alloy and CFRP. From results of cross tension test and observation of welding part, in case of shallow plunging depth of welding tool, generated heat was not sufficient to form welding part. On the other hand, in case of more deeper plunging depth of welding than thickness of thermoplastic sheet, Al alloy was directly contacted to CFRP, as a result, decrease in welding area. From result of measurement of axial load applied to the welding tool during the process, it is considered that higher axial load was generated to higher interfacial strength of CFRP/thermoplastic sheet and also tensile shear strength of Al alloy/ CFRP friction lap spot joint.</p>