Refinement and Coarsening of Grains Caused by Tensile-Shear Tests in Ultra-Fine Grained Cu Processed by Severe Plastic Deformation
-
- Matsutani Ryosuke
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- Miyajima Yoji
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- Onaka Susumu
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
この論文をさがす
説明
<p>Ultra-fine grained pure copper fabricated by equal-channel angular pressing was used as a sample. We made tensile-shear tests using specimens with notches cut from the sample and large shear deformation occurred between the notches. Microstructural changes between the notches caused by the large shear deformation were observed. Using micro scale lattices scribed on the surface of the specimen, we found both refinement and coarsening of grains caused by the large shear deformation. Although severe plastic deformation causes ultra-fine grained structure, it is known there is a limit of the grain refinement. The grain coarsening observed in the present study is considered to be the reason of the limit of the grain refinement caused by severe plastic deformation.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Japan Inst. Met. Mater. 82 (2018) 442–448.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 60 (5), 751-757, 2019-05-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001288133487872
-
- NII論文ID
- 40021879181
- 130007636531
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 029658331
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可