Pulse Anodization of Tantalum Oxide/Polypyrrole Film on Nanoporous Tantalum Anode for Solid Electrolytic Capacitors
-
- NAOI Katsuhiko
- Center of Future Nanomaterials Science, Institute of Symbiotic Science and Technology, Tokyo University of Agriculture and Technology
-
- OTA Yosuke
- Center of Future Nanomaterials Science, Institute of Symbiotic Science and Technology, Tokyo University of Agriculture and Technology
-
- MACHIDA Kenji
- Center of Future Nanomaterials Science, Institute of Symbiotic Science and Technology, Tokyo University of Agriculture and Technology
Bibliographic Information
- Other Title
-
- ナノポーラスタンタル陽極上での酸化タンタル/ポリピロール膜のパルス電解同時生成と電解キャパシタ
- ナノポーラスタンタル ヨウキョク ジョウ デ ノ サンカ タンタル ポリピロール マク ノ パルス デンカイ ドウジ セイセイ ト デンカイ キャパシタ
Search this article
Abstract
<p>Under a pulse anodization mode, a dielectric Ta2O5 film and a conducting polypyrrole film were formed on a nanoporous Ta pellet anode (average pore size: 250 nm, specific surface area: 4,000 cm2 g-1, capacitance: 50,000μFV g-1). At a first pulse, Ta metal was anodized to form dielectric Ta2O5 nano film (1.6~ 14 nm in thickness) on nano-porous Ta pellet. With subsequent pulses, the polypyrrole film was deposited uniformly and compactly (average thickness: 70~230 nm) on the Ta2O5/Ta nano-porous layer. The thickness of polypyrrole film was controlled by tuning current and charge of the pulse. The polypyrrole film on the Ta2O5/Ta nano-porous layer showed low resistivity of 2×10-1Ω persquare. By AC impedance analysis, low equivalent series resistance (400 mΩ at 100 kHz) was demonstrated for a sample electrolytic capacitor with nano-porous Ta2O5/Ta anode with polypyrrole coating layer.</p>
Journal
-
- Electrochemistry
-
Electrochemistry 73 (7), 496-501, 2005-07-05
The Electrochemical Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001288141314944
-
- NII Article ID
- 10014350785
-
- NII Book ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL BIB ID
- 7417121
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Allowed