CO<SUB>2</SUB>-CO混合ガスと平衡する酸化鉄融液の密度

DOI DOI Web Site Web Site Web Site 被引用文献5件 参考文献4件 オープンアクセス
  • Mori Kazumi
    Department of Iron and Steel Engineering, Faculty of Engineering, Nagoya University
  • Suzuki Kanae
    Department of Iron and Steel Engineering, Faculty of Engineering, Nagoya University

書誌事項

タイトル別名
  • Density of Iron Oxide Melt in Equilibrium with CO<sub>2</sub>-CO Gas Mixture
  • CO2-CO混合ガスと平衡する酸化鉄融液の密度
  • CO2-CO コンゴウ ガス ト ヘイコウ スル サンカテツユウエキ ノ ミツド
  • Density of Iron Oxide Melts in Equilibrium with CO<SUB>2</SUB>-CO Gas Mixtures

この論文をさがす

説明

Densities of iron oxide melts in equilibrium with CO2-CO gas mixtures have been measured by the Archimedean method employing the double-bob technique. The explored temperature range is 1450 to 1525°C and composition range is Fe3+/ΣFe=0.093 to 0.358. At constant temperatures densities of the melts decrease with increase of Fe3+ content. At higher Fe3+ contents this decrease of density becomes more gradual. At constant compositions densities decrease linearly with increase of temperature. Expansivities of the melts decrease with increase of Fe3+ content. The results are interpreted with a proposed model on the constitution of the melts. It is pointed out that oxygen ions are much more closely attracted to Fe3+ than to Fe2+ and this is responsible for the trends in the relations of both density and expansivity with composition.