自動車用超高強度TRIP型マルテンサイト鋼板のスポット溶接引張特性

書誌事項

タイトル別名
  • Spot Welded Tensile Properties in Automobile Ultrahigh Strength TRIP-aided Martensitic Steel Sheet
  • ジドウシャヨウ チョウコウキョウド TRIPガタ マルテンサイト コウバン ノ スポット ヨウセツ ヒッパリ トクセイ

この論文をさがす

説明

<p>Effect of heat-affected zone (HAZ) softening on tensile strength (TS) and total elongation (TEl) of spot welded ultrahigh strength TRIP-aided martensitic (TM) steel sheet was investigated for automobile applications. Tensile test was performed on an Instron type tensile testing machine at a crosshead speed of 3 mm/min (strain rate of 8.3×10–4 s–1), using spot welded specimen.</p><p>The results are as follows.</p><p>(1) The spot welded specimen at the current value (I) of 6.5 kA for the TM steel with the maximum stress (TS*) of 1450 MPa and the fracture elongation (TEl*) of 7.0% was superior to that of hot stamping steel (the HS1 steel), and it was found that the TS* and the TEl* for the TM steel possessed those of base metal specimen for the HS1 steel with the tensile strength (TS) of 1469 MPa and the total elongation (TEl) of 7.7%.</p><p>(2) The TRIP effect for the TM steel with an excellent strength-ductility balance (TS×TEl) of 14.4 GPa% (i.e. the tensile strength (TS) of 1532 MPa and the total elongation (TEl) of 9.4%) suppressed HAZ softening and was able to express a high maximum stress (TS*) of 1450 MPa for the TM steel of the spot welded specimen.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 106 (7), 438-447, 2020

    一般社団法人 日本鉄鋼協会

被引用文献 (2)*注記

もっと見る

参考文献 (4)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ