- Rapid Evaluation of Hydrogen Embrittlement Resistance for Spot-Welds of High Tensile Strength Steel Sheet by Slow Rate Tensile Shear Test under Hydrogen Charging Conditions
- スイソ チャージ カ テイソクド ヒッパリ セン ダンシケン ニ ヨル コウチョウリョク コウバン ノ スポット ヨウセツブ ノ ジンソク スイソゼイカ ヒョウカホウ
この論文をさがす
抄録
<p>Automobile manufacturers are accelerating adoption of spot welding of Advanced High-Strength-Steels (AHSS) sheets to reduce weight of automobile bodies. Rapid evaluation of the hydrogen embrittlement (HE) resistance for the spot-welds of AHSS sheets is required, since it is worried that the HE resistance of the nugget will deteriorate compared to the base metal due to the difference in microstructure caused by rapid cooling and solidification during spot welding. However, evaluation of the HE resistance for the spot-welds have not been established. In this study, we prepared spot-welded specimens using AHSS sheets and performed tensile shear tests with varying tensile rates under hydrogen charging to evaluate the relationship between diffusible hydrogen content and tensile shear strength. As a result, the tensile shear strength of spot welds decreased as the amount of diffusible hydrogen increased. The quasi-cleavage fractured surface and intergranular fractured surface were observed at the nugget and inside the crack generated at the nugget-heat affected zone interface. Furthermore, as the results of crack growth behavior and hydrogen thermal desorption spectroscopy analysis, hydrogen embrittlement in spot welds can be attributed to the stress-induced diffusion of hydrogen and the hydrogen trapped in dislocation and vacancy clusters at the crack tip.</p>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 85 (2), 75-83, 2021-02-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390005506401698048
-
- NII論文ID
- 130007974695
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 031285906
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可