- Corrosion behavior of galvanic couple between aluminum alloy and carbon steel with accelerated corrosion tests
- ソクシン フショク シケン ニ オケル アルミニウム ゴウキン/タンソコウ ノ ガルバニック フショク キョドウ
この論文をさがす
抄録
<p>We investigated the galvanic corrosion behavior of aluminum alloy in contact with carbon steel during accelerated corrosion testing by evaluating the galvanic current and corrosion morphology of the coupled specimen. Electrochemical polarization curve was acquired before and after accelerated corrosion testing, with galvanic current only detected for aluminum dissolution. Aluminum next to the carbon steel was more severely corroded than remote aluminum. Corrosion was also observed in the carbon steel, although its dissolution current was not detected. Galvanic corrosion behavior was found to be dependent on the duration of exposure to water and the chemical composition of the aluminum alloy. The galvanic corrosion of aluminum was not only affected by the connected metal and the environment to which it was exposed, but also by the distance from the connected metal, and was dependent on the ion concentration of the connected metal.</p>
収録刊行物
-
- 軽金属
-
軽金属 71 (2), 102-111, 2021-02-15
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390005888484762752
-
- NII論文ID
- 130007998314
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 031282022
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可