The Effect of the Oriented Structure on Mechanical Properties of Titanium Aluminide Fabricated by Electron Beam Melting
-
- Inoue Kana
- Department of Mechanical Systems of Engineering, Graduate School of Systems Design, Tokyo Metropolitan University
-
- Kakehi Koji
- Department of Mechanical Systems of Engineering, Graduate School of Systems Design, Tokyo Metropolitan University
Bibliographic Information
- Other Title
-
- 電子ビーム溶融法によって作製されたチタンアルミ合金の機械的特性に及ぼす組織配向の影響
- デンシ ビーム ヨウユウホウ ニ ヨッテ サクセイ サレタ チタンアルミ ゴウキン ノ キカイテキ トクセイ ニ オヨボス ソシキハイコウ ノ エイキョウ
Search this article
Abstract
<p>This study was conducted to reveal the relationship between the oriented microstructure and mechanical properties of Ti-48Al-2Cr-2Nb fabricated by electron beam melting (EBM). The microstructure observation in EBM sample showed that duplex structure/γ band layers fabricated by EBM process.</p><p>Tensile and creep tests were conducted for two kinds of samples fabricated by EBM. One was a sample in which loading direction was parallel to the building direction (vertical sample) and another was sample in which the loading direction was normal (horizontal sample). The tensile test showed anisotropic tensile properties at room temperature, 650℃ and 750℃. The tensile strengths of the vertical samples were inferior to the horizontal samples due to the oriented duplex structure with γ band layers. The creep lives were 206 h tested at 650℃/450 MPa and 298 h tested at 750℃/200 MPa in the vertical sample, whereas they were 332 h tested at 650℃/450 MPa and 326 h tested at 750℃/200 MPa in the horizontal sample; i.e., the creep test also showed the anisotropy of creep rupture life due to the oriented microstructure.</p>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 85 (5), 190-197, 2021-05-01
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390006352515411840
-
- NII Article ID
- 130008029641
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 031500185
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed