超音波処理による溶湯への微細気泡導入によるアルミニウム合金鋳物のひけ巣分散

DOI Web Site

書誌事項

タイトル別名
  • Dispersion of Shrinkage Cavity in Aluminum Alloy Castings Using Ultrasonic Melt Treatment for Generating Microbubbles
  • チョウオンパ ショリ ニ ヨル ヨウユ エ ノ ビサイ キホウ ドウニュウ ニ ヨル アルミニウム ゴウキン イモノ ノ ヒケ ソウ ブンサン

この論文をさがす

抄録

<p>  The size of defects in castings affects mechanical properties such as fatigue strength. These properties are the most important properties used for designing aluminum alloy casting components, and usually increase with decreasing size of internal defects. Large internal defects mainly form due to the volumetric shrinkage of melt at the last solidified position. In this study, we therefore examined the possibility of generating microbubbles in aluminum alloy melts for dispersing internal defects in castings.</p><p>  Ultrasonic treatment was used for generating nitrogen or argon microbubbles in the melt and was found to be suitable for forming fine gas porosities dispersed in castings. The fine gas remained in the melt for 3600 s, and the generated argon gas was detected from the porosities in the castings. The ultrasonic treatment could also remove inclusions and hydrogen in the melt. Moreover, the fine gas porosities in castings did not decrease the tensile strength of the castings.</p>

収録刊行物

  • 鋳造工学

    鋳造工学 93 (7), 394-399, 2021-07-25

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ