The reisistance of the mold is an important factor of the casting stress. On the other hand, several addivities (i.e. wood powder, pitch, coal powder and so on) are added for the purpose of the prevention against the sand burning or scab and the improvement of the properties at high temperature. In this experim ent, we added several addivities to the mold, and stdsudied the effects of these mold on the casting stress. The results obtained are as follows: (1) The resistance of the mold is decreased by adding wood powder, pitch and coal powder to the CO_2 mold. (2) As the strength of green sand mold is weak, the effect of the resistance of the mold on the casing stress is little. (3) In the case of adding wood powder to the C0_2 mold, the residual stress of the casting can decrease.

鋳物が鋳型内において凝固冷却する場合には，各部分が同一の冷却速度をもったり，自由な変形をすることはなく，一般に部材間で冷却速度が異なり，一部分の変形を無理に他の部分が阻止するような状態で常温に達するために，鋳造応力が生じる。この応力は，凝固冷却する際現われる部材間の亀裂や，ひずみの発生の原因となり，また鋳造後において，ひずみの発生，寸法変化などの欠陥の原因となる。このように鋳造応力は鋳物のひずみと密接な関係があり，その発生原因によって，鋳型抵抗により発生するひずみと不均一な冷却によって発生するひずみとに分けられる。そこでわれわれは先に，鋳型が鋳物の凝固およびその後の冷却の際の収縮に，大きな影響をおよぼすことに着目し，圧縮強さの異なる鋳型を用いて，その強度の差が，鋳造応力におよぽす影響について報告した。また従来一般に，木粉，ピッチ，石炭粉等の添加剤が焼着き，すくわれなどの防止，製品鋳肌の改善，鋳型の崩壊性の改善，高温性質の向上等の目的のために添加されている。そこで，本実験では，鋳型に木粉，ピッチ等を添加して，収縮ひずみ発生過程を調べ，それらの鋳型が鋳物の応力におよぽす影響を検討してみた。

identifier:富山大学工学部紀要，26

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ