The synthesis of Fe2N powder from FeC2O4 powder and their thermal decomposition behavior were studied, and their magnetic properties were investigated. FeC2O4powder, which is a starting material of iron nitride, was prepared by the precipitation method in ethanol solvent (FeCl2aq.-H2C2O4·EtOH), consequently fine powder was obtained. FezN powder was prepared by thermal decomposition of fine FeC2O4 powder under NH3 gas flow 410℃, and the pyrolysis temperature was lower than that of FeCP4 made from water solvent (FeClzaq.-(NH4)zCz0 4aq.). When the FezN powder was heated in air and Ar gas flow, the pyrolysis started at 150℃ and 350℃, respectively. Fe3N single phase was obtained by pyrolysis of FezN powder at 400℃ under Ar gas flow, and iron nItride transformation from paramagnetism to ferromaginetism was caused.
収録刊行物
-
- 埼玉大学地域共同研究センター紀要 = Report of Cooperative Research Center, Saitama University
-
埼玉大学地域共同研究センター紀要 = Report of Cooperative Research Center, Saitama University 2 51-54, 2002
埼玉大学地域共同研究センター
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390009224813730688
-
- NII論文ID
- 120006388412
-
- ISSN
- 13474758
-
- Web Site
- http://id.nii.ac.jp/1586/00016614/
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- JaLC
- IRDB
- CiNii Articles