Elastic Modulus of the Gel made from Interpenetrating Polymer Networks in Phase Separated State
この論文をさがす
抄録
Interpenetrated polymer network (IPN) of gelatin (Glt) and sodium polyalginate (Alg) is studied to prepare Alg gel, which is expected to be more uniform than that prepared directly at high added salt (NaCl) concen1rations, C_s. The mixed solution and IPNs are homogeneous at lower C_s. It was found that the mixed solution get phase separated around C_s =0.35M. The gels made from the phase separated solution were also investigated. The roughness of Alg gels prepared via IPN and directly at higher C_s is almost the same. It can be summarized that the phase separation was brought by higher Cs and it is not suitable to prepare uniform Alg gels with high.er C_s. It was pointed out that the Alg gels prepared with lower C_s via IPN shows narrower elastic modulus distribution than the higher ones.
収録刊行物
-
- Evergreen
-
Evergreen 1 (1), 1-5, 2014-03
九州大学グリーンテクノロジー研究教育センター
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390009224844851328
-
- NII論文ID
- 120005425177
- 40020037624
-
- DOI
- 10.5109/1440968
-
- ISSN
- 24325953
- 21890420
-
- HANDLE
- 2324/1440968
-
- NDL書誌ID
- 025391775
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可