MICROSTRUCTUAL CHANGE OF HARDENED CEMENT PASTE CONTAINING FLYASH BY POZZOLANIC REACTION
-
- UMEKI Shota
- NAGOYA UNIVERSITY, Graduate School of Environmental Studies(Furo-cho, Chikusa-ku, Nagoya-shi, Aichi 464-8601, Japan)
-
- MARUYAMA Ippei
- NAGOYA UNIVERSITY, Graduate School of Environmental Studies(Furo-cho, Chikusa-ku, Nagoya-shi, Aichi 464-8601, Japan) THE UNIVERSITY OF TOKYO, Graduate School of Engineering(7-3-1, Hongo, Bunkyo-ku, Tokyo 113-8656, Japan)
Bibliographic Information
- Other Title
-
- フライアッシュセメント硬化体のポゾラン反応に伴う微細構造変化
Abstract
<p>In this study, experiments were conducted over a period of one year using hardened ordinary Portland cement with fly ash substituted at 0, 7, and 14%. Microstructural changes of fly ash particles during pozzolanic reaction and precipitated C-A-S-H were observed using FE-SEM. The relationship between the water vapor and nitrogen specific surface areas and the pozzolanic reaction was summarized, and the water vapor BET surface area increased and the nitrogen BET surface area decreased as the pozzolanic reaction progressed. This indicates that the C-A-S-H produced by the pozzolanic reaction decreases the LD C-S-H, which is as dense as the HD C-S-H.</p>
Journal
-
- Cement Science and Concrete Technology
-
Cement Science and Concrete Technology 75 (1), 105-112, 2022-03-31
Japan Cement Association
- Tweet
Details 詳細情報について
-
- CRID
- 1390010292825700096
-
- ISSN
- 21873313
- 09163182
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed