Preparation of Nickel Catalysts Supported on Silica Particles by Collisions at a High Speed in a Gas-Phase Reactor
-
- Okada Yoshiki
- Graduate School of Science and Engineering, Kansai University
-
- Tsuji Ryusuke
- Graduate School of Science and Engineering, Kansai University
-
- Kinoshita Takuya
- Graduate School of Science and Engineering, Kansai University
この論文をさがす
抄録
<p>Silica (SiO2) particle-supported nickel (Ni) nanoparticles were prepared using a gas-phase synthesis method in which Ni nanoparticles, generated by hydrogen reduction of NiCl2, collide with SiO2 particles with a diameter of approximately 0.1 µm. Before collisions, SiO2 particles were heated in a gas-phase reactor to a temperature sufficiently high to soften their surfaces. When collisions between Ni and SiO2 particles occurred at a high speed of 38.6 m/s, Ni nanoparticles smaller than 10 nm could be captured by SiO2 particles heated to 1,723 K, and showed no signs of sintering on the SiO2 particle surfaces during heat treatment at a high temperature of 1,073 K.</p>
収録刊行物
-
- エアロゾル研究
-
エアロゾル研究 37 (3), 212-217, 2022-09-20
日本エアロゾル学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390012114415485952
-
- NII書誌ID
- AN10041511
-
- ISSN
- 1881543X
- 09122834
-
- NDL書誌ID
- 032403639
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
-
- 抄録ライセンスフラグ
- 使用不可