2-16 Production of high-strength coke from formed coal containing biomass resources
-
- TSUBOUCHI Naoto
- Hokkaido University
-
- WANG Yuting
- Hokkaido University
-
- MOCHIZUKI Yuuki
- Hokkaido University
-
- KONNO Saori
- Nippon Steel Corporation
-
- SHISHIDO Takahiro
- Kobe Steel, Ltd.
Bibliographic Information
- Other Title
-
- 2-16 バイオマス資源を含む成型炭からの高強度コークスの製造
Abstract
<p>Formed samples containing biomass (cedar wood powder) were heated first to 450-600°C at 10-40°C/min under pressure in an inert atmosphere and then to 800°C at 3°C/min under ambient pressure. The principal conclusions were summarized as follows: (1) Rapid heating treatment in the softening and melting temperature range of coal was effective in improving coke strength even in the presence of biomass. (2) Formed samples containing 3-5 % biomass without any pretreatment could produce coke of 4-5 MPa, though the coke strength was lower than that of standard blended coal. (3) It was found that biomass modified in 1-methylnaphthalene could maintain the coke strength at the standard blended coal level (approximately 9 MPa).</p>
Journal
-
- Proceedings of Conference on Coal Science
-
Proceedings of Conference on Coal Science 59 (0), 60-61, 2022-10-13
The Japan Institute of Energy
- Tweet
Details 詳細情報について
-
- CRID
- 1390012468146322304
-
- ISSN
- 24238309
- 24238295
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
-
- Abstract License Flag
- Disallowed