- Study on Factors Hindering the Single-phase Formation of Divalent-ion-stabilized W-type Ferrites
- 2カ イオン アンテイカ Wガタ Sr フェライト ノ タンソウカ ソガイ ヨウイン ノ ケントウ
この論文をさがす
抄録
<p>Me-substituted W-type ferrites (AMe2Fe16O27 with A = Sr, Ba, …, and Me = Co, Ni, Zn, Mg, …) can be obtained by standard solid state reaction but always contain secondary phases. Phase stability of SrMe2Fe16O27 with Me = Co, Ni, Zn, and Mg sintered in various oxygen pressures of pO2 = 0.2, 1, 10 and 387 atm were investigated using X-ray diffraction analysis, wavelength-dispersive X-ray (WDX) analysis, and transmission electron microscopy (TEM). WDX analysis revealed that the W-type ferrites are described as SrMe2-δFe16+δO27 because Fe3+ is partially reduced to Fe2+ even when synthesis is initiated from SrMe2Fe16O27. Increasing the oxygen pressure suppresses the reduction of Fe3+ and the formation of the secondary phases. In addition, TEM analysis shows that the SrCo2Fe16O27 single crystal is free of stacking faults. We conclude that the single-phase formation of the Me-substituted W-type ferrites is hampered by the discrepancy between initial and actual chemical composition caused by the appearance of Fe2+.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 69 (11), 455-460, 2022-11-15
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390012638729711616
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- HANDLE
- 2433/283241
-
- NDL書誌ID
- 032524495
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可