Al-Zn-Mg-Cu合金中のIMC粒子損傷に及ぼす水素の影響

DOI DOI Web Site Web Site Web Site 被引用文献4件 参考文献32件 オープンアクセス

書誌事項

タイトル別名
  • Influence of Hydrogen on the Damage Behavior of IMC Particles in Al–Zn–Mg–Cu Alloys

この論文をさがす

説明

<p>In recent years, it has been reported that intermetallic compound particles can suppress hydrogen embrittlement by hydrogen trapping. Some intermetallic particles in aluminum alloys, such as Al7Cu2Fe, have internal hydrogen trap sites; it is proposed that hydrogen embrittlement can be suppressed by preferential hydrogen partitioning in these sites. However, intermetallic compound particles act as fracture origin sites, and excessive addition degrades the mechanical properties of the material. In this study, we quantitatively evaluated the damage and decohesion behavior of intermetallic compound particles in high-hydrogen content 7XXX aluminum alloys by using in situ synchrotron radiation X-ray tomography. The results revealed that the hydrogen particles induced early high-strain localization, and the Al7Cu2Fe particles were damaged in that region due to its brittleness, resulting in early fracture. Hydrogen had no effects on the fracture and debonding behaviors of intermetallic compound particles, suggesting that the observed particle brittle fracture is dependent on their mechanical properties.</p><p> </p><p>This Paper was Originally Published in Japanese in J. JILM 72 (2022) 411–419. Abstract and the captions of Figs. 1, 2, 4, 5, 6, 7, 9 and 10 are slightly modified.</p>

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 63 (12), 1607-1616, 2022-12-01

    公益社団法人 日本金属学会

被引用文献 (4)*注記

もっと見る

参考文献 (32)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ