Enhancing CO<sub>2</sub> Mineralization Rate and Extent of Iron and Steel Slag via Grinding
-
- Myers Corey
- Lawrence Livermore National Laboratory
-
- Sasagawa Jun
- Waseda University
-
- Nakagaki Takao
- Faculty of Modern Mechanical Engineering, Waseda University
抄録
<p>Roughly 10% of the CO2 emissions from iron and steel making are attributable to the direct release of CO2 from the thermal decomposition of carbonates to produce flux, mainly CaO, used for impurity removal. Notably, these direct emissions remain even if carbon-based steelmaking is replaced by hydrogen-based steelmaking. After removing impurities from the molten metal, this flux becomes the solid waste product called ‘slag’, a primarily Ca-silicate material. The transformation of slag back into carbonates is thermodynamically spontaneous with negative ΔG in the ambient environment, meaning that ~10% of the CO2 emissions from iron and steel making could be negated if equipment and methods were developed to support CO2 mineralization. However, the rate of CO2 mineralization using slag is slowed by several environmental, geometric, and processing factors. We leverage an experimentally verified model of CO2 mineralization to determine how to efficiently accelerate the process. Increasing the crystallinity of slag, increasing the relative humidity, and reducing the grain size of slag particles provide the greatest increase in CO2 mineralization rate at the lowest energy penalty. Increasing the concentration of CO2 and the temperature provide only modest increases in the CO2 mineralization rate while incurring a substantial energy penalty. For steelmaking slags, CO2 mineralization represents low-hanging fruit as the current reuse pathways are low value. For ironmaking slag, replacing the production of amorphous slag for the cement industry with the production of crystalline slag for CO2 mineralization becomes financially preferable when a carbon price/tax exceeds 67.40 USD/t-CO2.</p>
収録刊行物
-
- ISIJ International
-
ISIJ International 62 (12), 2446-2453, 2022-12-15
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390012954685539968
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可