Influence of Initial Extruded Microstructures of Al–4.4Zn–1.4Mg Alloy Flat Bar on VDA Bendability
-
- Kaharudin Amalina Aina
- Department of Science of Technology Innovation, Nagaoka University of Technology
-
- Saeki Ran
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Takaya Mai
- R&D Center, UACJ Corporation
-
- Minoda Tadashi
- R&D Center, UACJ Corporation
-
- Homma Tomoyuki
- Department of Science of Technology Innovation, Nagaoka University of Technology Department of Mechanical Engineering, Nagaoka University of Technology
この論文をさがす
説明
<p>The bendability of extruded Al–4.4Zn–1.4Mg (mass%) alloy flat bars with 1.4 mm thickness having two types of microstructures which are fibrous and recrystallized is evaluated by a Verband der Automobilindustrie (VDA) bending test without pre-strain. The recrystallized specimen has better bendability than the fibrous one. The texture condition nearby the surfaces affects the VDA bendability the most. However, the microvoid formations also contribute in faster cracking phenomena during the load drop of the VDA bending test.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 64 (2), 421-428, 2023-02-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390013408149005056
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 032635732
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可