- Microstructure in subsurface and fatigue properties of shot peened maraging steel
抄録
<p>Rotating bending fatigue tests were carried out to investigate the effect of microstructure in subsurface on the fatigue properties of a shot peened maraging steel. The steel had a fine-grained microstructure formed at the surface layer with 50-70 μm in depth. Especially a thin surface layer showed a nano-size structure. A surface fracture occurred at high stress levels, while the combined fracture occurred due to coalescence of a surface crack and an internal one initiated independently with decreasing in stress level until 108 cycles. In all of the macroscopic fracture surfaces in the shot-peened specimen, a ring-shaped flat area was observed at the surface layer irrespective of the fracture mode and the depth of the area nearly corresponded to the one of the fine-grained microstructure. The formation mechanism of the ring-shaped area was explained from the initiation and propagation properties of a surface crack in the surface layer in connection with the microstructure.</p>
収録刊行物
-
- M&M材料力学カンファレンス
-
M&M材料力学カンファレンス 2022 (0), OS0313-, 2022
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390014093884689664
-
- ISSN
- 24242845
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可